Suitable for aesthetic and colorful coating of steel surfaces exposed to permanent high temperatures (200-600 °C). Low solvent content paint with satiny or glossy finish.
Stir well before use. Paint shall be applied onto oxide-free (shot blasted surface, grade Sa 2½ according to MSZ EN ISO 8501-1:2008 standard) and degreased surface in 15-25 µm dry film thickness. In case of Heat MIO paint, For achieving sufficient anticorrosion effect a minimum dry film thickness of 70-90 µm shall be applied. Coating dries within 20 minutes at 100-120° C, optimal character can be reached at 200° C in 30 minutes. Only after complete drying it is recommended to expose the paint to higher temperatures by keeping an even rate of heat up.
Our R&D Department elaborates paint formulations for industrial use. Primary task is to realize FKI's own product development targets. Technical Service lab is part of the R&D department, which adjusts the paint parameters to customers' requirements and renders direct technical assistance.
We take part in national and international development projects in cooperation with industrial partners and university research teams.
Research and DevelopmentThe aim of the paint industry experts' work is to ensure high quality surface-protection job for the customers. The preconditions of the successful execution of painting and surface-protection process are the elaboration of the technology most suitable for on-site needs, the correct choice of the coating and the monitoring of the execution.
The tests required for our expert activities are carried out according to the current MSZ EN ISO standards.
Expert activityDevelopment engineer/ Technical Service Unit
+36 1 4328844 horvath.szilvia[kukac]festekkutato[d0t]hu
Please feel free to contact our colleagues or call us
on the following number: +36 1 432 88 31